Analisis Uji Bending Pada Komposit Fiberglass Dan Hibiscus Cannabius Dengan Metode Hand Lay-up Dan Vacuum Assisted Resin Infusion (VARI) Sebagai Alternatif Pada Skin Vertical Stabilizer Pesawat Grob G 120 TP
DOI:
https://doi.org/10.54706/senastindo.v7.2025.456Kata Kunci:
Komposit, Fiberglass, Hand Lay-UpAbstrak
Penelitian ini menganalisis kekuatan lentur (bending strength) komposit berbahan fiberglass dan serat alami Hibiscus Cannabius (kenaf) sebagai alternatif material skin vertikal stabilizer pesawat Grob G 120 TP. Spesimen dibuat dengan dua metode, yaitu Hand Lay-Up dan Vacuum Assisted Resin Infusion (VARI), menggunakan variasi 100% fiberglass dan campuran fiberglass–kenaf 50:50, kemudian dibandingkan dengan material asli berbahan carbon fiber. Pengujian dilakukan sesuai standar ASTM D790. Hasil menunjukkan material asli memiliki kekuatan tertinggi 607 MPa, diikuti fiberglass Hand Lay-Up 559 MPa, fiberglass VARI 368 MPa, fiberglass–kenaf VARI 352 MPa, dan fiberglass–kenaf Hand Lay-Up 218 MPa. Berdasarkan hasil tersebut, komposit yang diuji belum dapat menggantikan carbon fiber karena nilai kekuatan bending masih lebih rendah.
Unduhan
Referensi
[1] Callister, W. D., & Rethwisch, D. G. (2013). Materials Science and Engineering: An Introduction. 9th Edition. John Wiley & Sons, New York.
[2] Sulistijono, D. E. (2012). Teknologi Material Komposit. Yogyakarta: Akademi Angkatan Udara Press.
[3] Saba, N., Jawaid, M., & Alothman, O. Y. (2015). A Review on Mechanical Properties of Kenaf Fiber Reinforced Polymer Composites. Journal of Reinforced Plastics and Composites, 34(17), 1341–1350.
[4] Nugroho, T. (2016). Kajian Kekuatan Mekanik Material Fiberglass. Politeknik Negeri Bandung.
[5] ASTM D790-17. (2017). Standard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials. ASTM International, West Conshohocken, PA.
[6] Schwartz, M. M. (1983). Composite Materials Handbook. McGraw-Hill, New York.
[7] Mohammed, L., Ansari, M. N. M., Pua, G., Jawaid, M., & Islam, M. S. (2015). A Review on Natural Fiber Reinforced Polymer Composite and Its Applications. International Journal of Polymer Science, 2015, 243947.
[8] Pickering, K. L., Efendy, M. A., & Le, T. M. (2016). A Review of Recent Developments in Natural Fibre Composites and Their Mechanical Performance. Composites Part A: Applied Science and Manufacturing, 83, 98–112.
Unduhan
Diterbitkan
Cara Mengutip
Terbitan
Bagian
Kategori
Lisensi
Hak Cipta (c) 2025 Galatia Kevin Putra Aritya, Dedy Eko Sulistiyono
Artikel ini berlisensiCreative Commons Attribution-ShareAlike 4.0 International License.